Spectrum Title	Formula	Edge	Min Energy	Max Energy	Resolution	Source & Purity	Spectrum Type	Date Submitted
HoS(Se)-TaS2(Se) Misfit Nanotube	HoS(Se)-TaS₂(Se)	S_K, Se_L1, Se_L2,3, Ta_M4,5, Ho_M4,5	1124.8 eV	2635.5 eV	2.0 eV		Core Loss	2018-01-15
LaS(Se)-TaS2(Se) Misfit Nanotube	LaS(Se)-TaS₂(Se)	Se_L2,3, Se_L1, La_M4,5, Ta_M4,5	524.8 eV	2008.1 eV	2.0 eV		Core Loss	2018-01-15
La0.7Sr0.3MnO3 Film On SrTiO3-(111) Substrate	La_0.₇Sr_0.₃MnO₃	Mn_L2,3, Mn_L1, O_K, La_M4,5	410 eV	920.8 eV	0.7 eV		Core Loss	2016-02-10
CaCoO Misfit Nanotube	CaCoO₂−CoO₂	Co_L2,3, O_K, Ca_L2,3, Ca_L1	254.8 eV	1099.6 eV	1.5 eV		Core Loss	2016-06-12
TbS-CrS2 Misfit Nanotube	TbS-CrS₂	S_L2,3, S_L1, Cr_L2,3, Tb_N4,5	112.6 eV	673.5 eV	0.6 eV		Core Loss	2015-11-29
MLC Nanotube YS-TaS2	(YS)_1.₂-TaS₂	Y_L1, Y_L2,3, Ta_M4,5, S_K	1700 eV	2574 eV	1.8 eV	Nanotube synthesized by chemic…	Core Loss	2023-10-18
Lanathanum Cobalt Oxide	LaCoO₃	O_K, La_M4,5, Co_L2,3, Co_L1	455 eV	966.5 eV	2.0 eV	stoechiometric phase	Core Loss	2008-01-19
Zinc Sulfide	ZnS	Zn_M2,3, S_L1, S_L2,3	61.8 eV	964.3 eV	1.0 eV		Core Loss	2008-01-29
SrTiO3	SrTiO₃	Ti_L2,3, Ti_L1, O_K	410 eV	920.8 eV	0.7 eV		Core Loss	2016-02-10
Niobium Oxide	Nb₂O₅	Nb_M2,3, Nb_M4,5, O_K	136.9 eV	806.4 eV	1.3 eV		Core Loss	2008-02-15
Niobium Oxide NbO2	NbO₂	Nb_M2,3, Nb_M4,5, O_K	120 eV	789.5 eV	1.3 eV		Core Loss	2008-02-15
Cerium Praseodymium Mixed Oxide Supported On Al2O3 Doped With La2O3	CePrOx/Al₂O₃-La₂O₃	La_M4,5, Ce_M4,5, Pr_M4,5	758.1 eV	1065 eV	-		Core Loss	2007-11-19
MLC Nanotube (Y,La)S-TaS2	((Y_{_0.₂} La{_0.₈})S)_1.₁₆-TaS_₂	Y_L2,3, S_K, Ta_M4,5	1700 eV	2574 eV	1.8 eV	Nanotube synthesized by chemic…	Core Loss	2023-11-06
Ta2O5 – Amoprhous	Ta₂O₅	O_K, Ta_N2,3, Ta_M4,5	150 eV	3147 eV	1.0 eV		Core Loss	2020-05-18
La2NiO4 – Structure Of K2NiF4	La₂NiO₄	O_K, Ni_L2,3, La_M4,5	424 eV	934.5 eV	0.2 eV	Monocristalline	Core Loss	2020-09-17
SrCoO Misfit NT	SrCoO	O_K, Co_L2,3, Sr_M2,3	235.8 eV	923.2 eV	2.0 eV		Core Loss	2016-12-19
Zinc Oxide	ZnO	O_K, Zn_L1, Zn_L2,3	415.1 eV	1313.1 eV	1.0 eV	Stoichiometric ZnO powder	Core Loss	2008-01-21
Chromium Monocarbide	CrC	C_K, O_K, Cr_L2,3	235 eV	636.7 eV	0.8 eV	Ultrahard CrC+a-C:H film (CVD)…	Core Loss	2008-01-30
Zr	Zircaloy-₄	Zr_L2,3, Zr_L1	1801.6 eV	3848.6 eV	0.5 eV	Commercial alloy	Core Loss	2017-07-05
Ti-ferrite (spinel)	Fe₂TiO₅	Ti_L2,3, O_K	423.6 eV	579.4 eV	2.0 eV	prepared by soft chemistry >99…	Core Loss	2005-04-20
Calcium Titanate (perovskite Structure)	CaTiO₃	Ti_L2,3, O_K	400 eV	604.2 eV	1.0 eV	commercially available powder	Core Loss	2007-12-05
Silicon Nitride	Si₃N₄	Si_L2,3, N_K	50 eV	719.5 eV	1.0 eV	Powder	Core Loss	2008-01-21
Molybdenum	Mo	Mo_L2,3, Mo_L1	1805.5 eV	3852.5 eV	0.5 eV	Sputtered thin film	Core Loss	2017-07-05
Lanthanum Cobalt Oxide	LaCoO₃	La_N4,5, Co_M2,3	-50 eV	461.5 eV	2.0 eV	stoechiometric phase	Low Loss	2008-01-19
Cerium Praseodymium Mixed Oxide	CePrOx	Ce_M4,5, Pr_M4,5	853.2 eV	1057.8 eV	-		Core Loss	2007-11-19
ZrO2	ZrO₂	Zr_L1, Zr_L2,3	1802.5 eV	3849.5 eV	0.5 eV	oxidised Zircaloy-4 in monocli…	Core Loss	2017-07-05
MoO2	MoO₂	Mo_L1, Mo_L2,3	1805 eV	3852 eV	0.5 eV	Sigma Aldrich	Core Loss	2017-07-05
Ge	Ge	Ge_L1, Ge_L2,3	713.3 eV	1724.8 eV	0.5 eV	Ge wafer	Core Loss	2016-11-25
Chromium Oxide (Chromia)	Cr₂O₃ (alpha)	O_K, Cr_L2,3	510.1 eV	612.4 eV	0.8 eV	Chromia powder from Sigma Aldr…	Core Loss	2008-01-08
Oxidized-graphenic Nanoplatelets Obtained From Bamboo – High Oxygen	C-O	C_K, O_K	211.7 eV	623.2 eV	0.8 eV		Core Loss	2016-08-24
Oxidized-graphenic Nanoplatelets Obtained From Bamboo – Low Oxygen	C-O	C_K, O_K	201.3 eV	616.8 eV	0.8 eV		Core Loss	2016-08-24
Hexagonal Boron Nitride	BN (hex)	B_K, N_K	113.5 eV	625 eV	1.2 eV	Aldrich powder	Core Loss	2007-11-12
Boron Nitride Single Wall Nanotube	BN	B_K, N_K	144.1 eV	743 eV	0.7 eV		Core Loss	2008-02-07
Calcium Titanate (polycrystalline Layer)	CaTiO₃	Ti_M2,3	0.1 eV	61.5 eV	0.2 eV	CaTiO3 sputter target 99.99% P…	Low Loss	2016-05-10
Strontium Titanate	SrTiO₃	Ti_L2,3	382.5 eV	689.4 eV	1.2 eV	single crystal	Core Loss	2007-11-12
Titanium Dioxide	TiO₂ (anatase)	Ti_L2,3	447.5 eV	498.7 eV	0.7 eV	Aldrich powder	Core Loss	2007-11-12
Titanium Dioxide	TiO₂ (amorphous)	Ti_L2,3	447.7 eV	498.9 eV	0.7 eV	University of Antwerp (powder)…	Core Loss	2007-11-12
Nickel Titanium	Ti₃Ni₄	Ti_L2,3	342 eV	1365 eV	1.0 eV	Nickel Titanium memory shape a…	Core Loss	2007-11-12
Titanium Dioxide (rutile Structure)	TiO₂	Ti_L2,3	403.8 eV	608 eV	1.2 eV		Core Loss	2008-01-21
Titanium	Ti	Ti_L2,3	435 eV	568.6 eV	-	Ti substrate	Core Loss	2008-01-21
Strontium Titanate	SrTiO₃	Ti_L2,3	438.3 eV	624 eV	-	STO substrate (perovskite mult…	Core Loss	2008-03-04
SrTiO3-(111)	SrTiO₃	Ti_L2,3	-22.4 eV	105091.7 eV	0.7 eV		Core Loss	2016-08-27
SrTiO3-(111), Light Beam Damage	SrTiO₃	Ti_L2,3	-8.1 eV	85585.1 eV	0.7 eV		Core Loss	2016-08-27
SrTiO3-(111), Heavy Beam Damage	SrTiO₃	Ti_L2,3	-16 eV	77981.9 eV	0.7 eV		Core Loss	2016-08-27
SrTiO3-(111)	SrTiO₃	Ti_L2,3	392 eV	494.4 eV	0.7 eV		Core Loss	2016-08-27
Silicon Nitride Alpha	Si₃N₄ (alpha)	Si_L2,3	90.3 eV	173.5 eV	1.1 eV	CVD	Core Loss	2005-04-20
Silicon Dioxide Amorphous	a-SiO₂	Si_L2,3	90.3 eV	173.5 eV	1.1 eV		Core Loss	2005-04-20
Silicon Carbide 6H(hexagonal)	SiC(₆H)	Si_L2,3	88.5 eV	190.4 eV	1.0 eV	single crystal	Core Loss	2005-04-20
Silicon Carbide 6H(hexagonal)	SiC(₆H)	Si_L2,3	90.3 eV	173.5 eV	1.0 eV	single crystal	Core Loss	2005-04-29
Silicon	Si	Si_L2,3	90.3 eV	173.6 eV	1.1 eV	wafer	Core Loss	2007-11-19

Showing spectra 1 to 50 out of 199.