Browse Spectra

Active Filters: None

Spectrum Title	Formula	Edge	Min Energy	Max Energy	Resolution	Source & Purity	Spectrum Type	Date Submitted
MoO3	MoO₃		183.2 eV	586.3 eV	2.2 eV	Acros, 99%	Core Loss	2015-09-13
SrCoO Misfit NT	SrCoO	O_K, Co_L2,3, Sr_M2,3	235.8 eV	923.2 eV	2.0 eV		Core Loss	2016-12-19
Ti-ferrite (spinel)	Fe₂TiO₅	Ti_L2,3, O_K	423.6 eV	579.4 eV	2.0 eV	prepared by soft chemistry >99…	Core Loss	2005-04-20
Lanthanum Cobalt Oxide	LaCoO₃	La_N4,5, Co_M2,3	-50 eV	461.5 eV	2.0 eV	stoechiometric phase	Low Loss	2008-01-19
Ti-ferrite (spinel)	Fe₂TiO₅	Fe_L2,3	653.6 eV	809.4 eV	2.0 eV	prepared by soft chemistry >9…	Core Loss	2005-04-20
Lanathanum Cobalt Oxide	LaCoO₃	O_K, La_M4,5, Co_L2,3, Co_L1	455 eV	966.5 eV	2.0 eV	stoechiometric phase	Core Loss	2008-01-19
Ti-ferrite (spinel)	Fe₂TiO₅		-44.4 eV	159.4 eV	2.0 eV	prepared by soft chemistry >9…	Low Loss	2005-04-20
Vanadium	V	V_K	5365 eV	6384 eV	2.0 eV	Vanadium metal	Core Loss	2005-04-20
LaS(Se)-TaS2(Se) Misfit Nanotube	LaS(Se)-TaS₂(Se)	Se_L2,3, Se_L1, La_M4,5, Ta_M4,5	524.8 eV	2008.1 eV	2.0 eV		Core Loss	2018-01-15
HoS(Se)-TaS2(Se) Misfit Nanotube	HoS(Se)-TaS₂(Se)	S_K, Se_L1, Se_L2,3, Ta_M4,5, Ho_M4,5	1124.8 eV	2635.5 eV	2.0 eV		Core Loss	2018-01-15
Chromium	Cr	Cr_K	5868 eV	6887 eV	2.0 eV	Chromium metal	Core Loss	2005-04-20
MLC Nanotube (Y0.6La0.4)S-TaS2	((Y_{_0.₆} La{_0.₄})S)_1.₁₈-TaS_₂		1700 eV	2574 eV	1.8 eV	Nanotube synthesized by chemic…	Core Loss	2023-11-06
Cubic Boron Nitride	c-BN	N_K	381.1 eV	462.2 eV	1.8 eV	high pressure synthesis (G. De…	Core Loss	2005-04-20
Diamond	C	C_K	265.6 eV	367.5 eV	1.8 eV	CVD diamond	Core Loss	2005-04-20
Diamond	C		-11.4 eV	90.5 eV	1.8 eV	CVD diamond	Low Loss	2005-04-20
MLC Nanotube YS-TaS2	(YS)_1.₂-TaS₂	Y_L1, Y_L2,3, Ta_M4,5, S_K	1700 eV	2574 eV	1.8 eV	Nanotube synthesized by chemic…	Core Loss	2023-10-18
MLC Nanotube (Y,La)S-TaS2	((Y_{_0.₂} La{_0.₈})S)_1.₁₆-TaS_₂	Y_L2,3, S_K, Ta_M4,5	1700 eV	2574 eV	1.8 eV	Nanotube synthesized by chemic…	Core Loss	2023-11-06
Cubic Boron Nitride	c-BN	B_K	167.7 eV	262.2 eV	1.8 eV	synthesis @ high pressure (G. …	Core Loss	2005-04-20
Aluminium Nitride	AlN	Al_K	1533.4 eV	1635.3 eV	1.6 eV	AlN fritt	Core Loss	2005-04-20
Aluminium Nitride	AlN		-14.5 eV	87.4 eV	1.6 eV	AlN fritt	Low Loss	2005-04-20
Diamond	C		-6.1 eV	44.8 eV	1.6 eV	CVD diamond	Low Loss	2005-04-20
Aluminium Nitride	AlN	N_K	368.3 eV	470.2 eV	1.6 eV	AlN fritt	Core Loss	2005-04-20
MoO2	MoO₂		313.4 eV	591.6 eV	1.5 eV	Commercial	Core Loss	2015-09-13
MoO2	MoO₂		-36.6 eV	241.6 eV	1.5 eV	Commercial	Low Loss	2015-09-13
MoO3	MoO₃		316 eV	594.2 eV	1.5 eV		Core Loss	2015-09-13
MoO3	MoO₃	Mo_N2,3	-34 eV	244.2 eV	1.5 eV		Low Loss	2015-09-13
Zero-loss C-FEG Hitachi Disp 0.214 EV	No		-63.6 eV	206.1 eV	1.5 eV		Zero Loss	2015-09-13
CaCoO Misfit Nanotube	CaCoO₂−CoO₂	Co_L2,3, O_K, Ca_L2,3, Ca_L1	254.8 eV	1099.6 eV	1.5 eV		Core Loss	2016-06-12
Niobium Oxide	Nb₂O₅	Nb_M2,3, Nb_M4,5, O_K	136.9 eV	806.4 eV	1.3 eV		Core Loss	2008-02-15
Niobium Oxide NbO2	NbO₂		-22.5 eV	647 eV	1.3 eV		Low Loss	2008-02-15
Niobium Oxide NbO2	NbO₂	Nb_M2,3, Nb_M4,5, O_K	120 eV	789.5 eV	1.3 eV		Core Loss	2008-02-15
Niobium Oxide	Nb₂O₅		-49.8 eV	619.7 eV	1.3 eV		Low Loss	2008-02-15
Amorphous Carbon 500ºC, 15 Min	a-C:H	C_K	229.1 eV	331.5 eV	1.2 eV		Core Loss	2016-12-20
Hexagonal Boron Nitride	BN (hex)		-61.5 eV	450 eV	1.2 eV	Aldrich Powder	Low Loss	2007-11-12
Oxidised Amorphous Carbon, 500ºC, 2500 Min	a-C:H,O	C_K	242.9 eV	345.2 eV	1.2 eV		Core Loss	2016-12-20
Strontium Titanate	SrTiO₃		-36 eV	270.9 eV	1.2 eV	single crystal	Low Loss	2007-11-12
Strontium Titanate	SrTiO₃	Ti_L2,3	382.5 eV	689.4 eV	1.2 eV	single crystal	Core Loss	2007-11-12
Graphite	C	C_K	268.3 eV	370.2 eV	1.2 eV	natural graphite from Madagasc…	Core Loss	2005-04-20
Hexagonal Boron Nitride	BN (hex)	B_K, N_K	113.5 eV	625 eV	1.2 eV	Aldrich powder	Core Loss	2007-11-12
Graphite	C		-10.7 eV	91.2 eV	1.2 eV	natural graphite from Madagasc…	Low Loss	2005-04-20
Boron Carbide	B₄C		-14.4 eV	87.5 eV	1.2 eV	Commercial powder Aldrich	Low Loss	2005-04-20
Titanium Dioxide (rutile Structure)	TiO₂		-16.8 eV	187.4 eV	1.2 eV		Low Loss	2008-01-21
Boron Carbide	B₄C	B_K	168 eV	269.9 eV	1.2 eV	Commercial powder Aldrich	Core Loss	2005-04-20
Titanium Dioxide (rutile Structure)	TiO₂	Ti_L2,3	403.8 eV	608 eV	1.2 eV		Core Loss	2008-01-21
Magnesium Carbonate	MgCO₃	O_K	512 eV	614.3 eV	1.2 eV	commercial powder Merck	Core Loss	2005-04-20
Boron Carbide	B₄C	C_K	267.7 eV	369.6 eV	1.2 eV	Commercial powder Aldrich	Core Loss	2005-04-20
Magnesium Carbonate	MgCO₃	C_K	245.2 eV	347.5 eV	1.2 eV	commercial powder Merck	Core Loss	2005-04-20
99.99% Nickel Metal	Ni	Ni_L2,3	846.5 eV	897.2 eV	1.1 eV		Core Loss	2005-05-26
Nickel Monoxide	NiO	Ni_L2,3	847.4 eV	898.1 eV	1.1 eV	99.99% NiO	Core Loss	2005-05-26
Silicon Nitride Alpha	Si₃N₄ (alpha)		-12.7 eV	89.2 eV	1.1 eV	CVD	Low Loss	2005-04-20

Showing spectra 1 to 50 out of 290.